Ultramid® Endure D3G10 BK20560
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xh5GZA_Ultramid-Endure-D3G10-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Endure D3G10 BK20560 is a glass fiber reinforced injection molding grade with high stiffness, very good flowability, and excellent heat aging resistance up to at least 220 degC (428 degF). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.77 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 3.7 to 4.3 | % | |
| Equilibrium, 23°C, 50% RH | 1.0 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 17400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 240 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 16200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 375 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 88 | kJ/m² | |
| 23°C | 97 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 19 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 259 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 248 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIG4002 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sindustris PP H1502 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Unichem 7011C2-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| MAJORIS FN068 - 8139 | AD majoris | PP Copolymer | MAJORIS |
| Sylvin 9925-70UV Grey 9526 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |