RTP 1600
| Category: | PAS , Polyarylsulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xgafzs_RTP-1600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.9 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 to 360 | °C | |
| Middle Temperature | 354 to 371 | °C | |
| Front Temperature | 366 to 385 | °C | |
| Mold Temperature | 93.3 to 163 | °C | |
| Injection Pressure | 68.9 to 124 | MPa | |
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 60 to 90 | rpm | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP562T | LyondellBasell Industries | PP Homopolymer | Moplen |
| BMC 840-6558 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| Cri-Line GP-615-65-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Huaxia Shenzhou FKM DS2601-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |