Altuglas® MI-2T
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Altuglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XgBwce_Altuglas-MI-2T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Altuglas® MI-2T is a Polymethyl Methacrylate Acrylic product. It can be processed by blow molding, extrusion, injection molding, profile extrusion, or thermoforming and is available in Asia Pacific or Europe. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1180 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (230°C/3.8 kg) | 3.00 | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 2.0 | % | |
| Equilibrium | 0.31 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | 78.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 6 |
| Nominal strain at break | 10 | % | ISO 527-2 7 |
| Tensile Creep Modulus | ISO 899-1 8 | ||
| 1 hr | 2600 | MPa | |
| 1000 hr | 1700 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength (23°C) | 3.00 | kJ/m² | ISO 179/1eA 9 |
| Charpy impact strength (23°C) | 25.0 | kJ/m² | ISO 179/1eU 10 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 11 | ||
| 0.45 MPa | 102 | °C | |
| 1.8 MPa | 99.0 | °C | |
| Vicat Softening Temperature (50°C/h, B (50N)) | 107 | °C | ISO 306 12 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 13 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 14 |
| Volume resistivity | 1.0E+13 | ohms·m | IEC 60093 15 |
| Electric strength | 19 | kV/mm | IEC 60243-1 16 |
| Relative Permittivity | IEC 60250 17 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 18 | ||
| 100 Hz | 0.050 | ||
| 1 MHz | 0.040 | ||
| Comparative tracking index | 600 | IEC 60112 19 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | ISO 1210 20 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHI211 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| 4POM® 23I15200 | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| CompaMid® PA 6.6 GF 30 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| HFFR 2004 | Teknor Apex Company | Polyolefin, Unspecified | HFFR |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8271 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |