Lucent PP TPP-140
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lucent Polymers, Inc. |
| Trademark: | Lucent PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xff3Md_Lucent-PP-TPP-140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% Talc Filled, Homopolymer Polypropylene Melt Flow Adjustable for Application Colors Available Add "U" for UV Stabilized Add "H" for Heat Stabilized Meets TSM-5601G-3A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 3590 | MPa | ASTM D790 |
| Flexural Strength | 53.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaflex® TPE-S 60A 5123 FR S1 | Bada AG | TPE | Badaflex® |
| Hostacom ETA5081 | LyondellBasell Industries | TPO (POE) | Hostacom |
| Karina STRAW PVC COMPOUND 800-38/ 14-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® PPC-20-2.0-A | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Pearlthane® CLEAR 15N80 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |