EMERGE™ PC 8900
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XfTS7x_EMERGE-PC-8900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMERGE™ PC 8900 is translucent, ignition-resistant Polycarbonate resin. This resin halogen free flame retardant and is intended to comply with global environmental standards. It is an easy processing PC resin suitable for use in IR PC film or sheet extrusion. It has UL 94 flammability rating of 0.5 mm V-0. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2020 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 67.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 3.20 mm, Injection Molded) | 110 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2920 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.20 mm, Injection Molded) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 98.9 | °C | |
| 1.8 MPa, Unannealed | 86.1 | °C | |
| Vicat Softening Temperature | 114 | °C | ASTM D1525 1 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 12 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(0.500 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 40K | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Rotolon 100 | Greene, Tweed & Co. | PTFE | Rotolon |
| Shinblend® A782 | Shinkong Synthetic Fiber Corp. | PC+ABS | Shinblend® |
| EVALENE® PP PHT0171 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| OTECH PVC OM5513-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |