SUPRAN® LFT PP 1380
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® LFT PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xeq3ne_SUPRAN-LFT-PP-1380.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 83% long glass fiber reinforced Polypropylene. High Stiffness, high toughness & superior mechanical balanced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.92 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D648 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 14400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 510 | J/m | |
| 23°C | 510 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 165 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 81 T 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Geon™ Vinyl Flexible 86143 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LARIPUR® LPR 9020 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Karina GRAY PVC COMPOUND 900-18/121-AYR-AC (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAB B902 (16% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |