Lotryl® 24MA02
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xd81og_Lotryl-24MA02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 24MA02 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 24MA02 can be used for applications where softness, flexibility and polarity are required. Typical applications are flexible film, polyesters modification and cable compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| 23°C | 0.940 | g/cm³ | ISO 1183 |
| -- | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 to 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 23.0 to 26.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 79 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 12.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 800 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 18.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 49.0 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 68.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAPLAST® UPA 63 | RASCHIG GmbH | Polyester, TS | SUPRAPLAST® |
| CoolPoly® D5110 | Celanese Corporation | PPS | CoolPoly® |
| Hostaform® C 9021 TF | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Kumho PS GP 150K | Korea Kumho Petrochemical Co., Ltd. | PS (GPPS) | Kumho PS |
| RTP 199 X 138766 Z EG | RTP Company | PP, Unspecified | RTP |