Hylex® P1025 L2 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xclp8C_Hylex-P1025-L2-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hylex® P1025 L2 HB is a Polycarbonate (PC) material. It is available in North America. Important attributes of Hylex® P1025 L2 HB are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 72 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 132 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 3.18 mm, In Air) | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (3180 µm) | 88.0 | % | ASTM D1003 |
| Haze (3180 µm) | 1.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® RG-10180 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Witcom ABS 3S | Witcom Engineering Plastics B.V. | ABS | Witcom ABS |
| Kumho SBR 1500 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| OXNILON 66 20PTFE | Oxford Polymers | Nylon 66 | OXNILON 66 |
| LNP™ LUBRICOMP™ KFL36 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |