InnoPlus LL7420A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZnuzH_InnoPlus-LL7420A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus LL7420A resin is a linear low density polyethylene with butene comonomers, without slip and antiblock. This grade offers an outstanding excellent draw down in both blown and cast film processing. Films extruded from InnoPlus LL7420A have high tensile, gloss and good toughness properties. It can be used for blending with other polyethylene types, such as HDPE and LDPE. InnoPlus LL7420A is recommended for producing the stretch wrap films, liners, industrial bags, refuse sacks and garbage bags. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 10.0 | MPa | ASTM D638 |
| Fracture, molding | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 900 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 290 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 195 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 220 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 900 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 85 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 100 | g | ASTM D1922 |
| TD : 25 µm, blown film | 320 | g | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 390 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 121 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 160 - 180 °C for extruder and 170 - 190 °C for die zone. (blown film) 210 - 270 °C for extruder and 260 - 270 °C for die zone. (cast film) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2807 | Covestro - Polycarbonates | PC | Makrolon® |
| Baoding 76E85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Greenflex® ML 60 F | Versalis S.p.A. | EVA | Greenflex® |
| MAJORIS CFR210R | AD majoris | PP, Unspecified | MAJORIS |
| Moplen EP300K | LyondellBasell Industries | PP Copolymer | Moplen |