AZDEL™ R301B01N
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZkwmk_AZDEL-R301B01N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Azdel® R301B01N is a random oriented needled continuos glass fibre mat material. This polypropylene composite material features high properties and homogeneous fibre distribution. This material is typically used for standard semi-structural applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.32 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 70 | kJ/m² | ISO 179/2fnU |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| 4.00, energy to power peak | 10.0 | J | ISO 6603-2 |
| 4.00, total impact penetration energy | 30.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (4.00 mm) | 3800 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 166 | °C | ISO 3146 |
| Additional Information |
|---|
| Mass Per Unit Area, Azdel Test Method: 4.300 kg/m²Thickness, Azdel Test Method: 3.9 mmDensity, ISO 1183 Test Method: 1.10 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.14 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 114 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 4.3e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.3e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® W 43006 | Reliance Industries Limited | HDPE | RELENE® |
| Shinko-Lac® ASA S450 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Grivory® HTV-4H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| LNP™ STAT-KON™ RE0039 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ EX93452 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |