Bergadur™ PB40 G10 H U colored
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergadur™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZgLLG_BergadurPB40G10HUcolored.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergadur™PB40 G10 H U colored is a polybutene terephthalate (PBT) product, which contains a 10% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.55 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 15 - 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm, Injection Molded) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded) | > 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Comparative Tracking Index (CTI) | 225 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.4 to 3.0mm) | V-0 | Internal method | |
| Glow Wire Flammability Index (0.4 to 3.0mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Mold Temperature | 75 - 95 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G55A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Xuchuan 2006/B-8016 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| APEX® 75-9351A-102 | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ STAT-KON™ PFD06 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-KON™ |
| Hostacom TKC 451N D11449 | LyondellBasell Industries | PP Copolymer | Hostacom |