Akulon® S223-GM35
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZBGu8_Akulon-S223-GM35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® S223-GM35 is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber and 25% mineral. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 5000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 76.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 7700 | -- | MPa | ISO 178 |
| Flexural Stress | 175 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.7 | 2.9 | kJ/m² | |
| 23°C | 4.3 | 6.2 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 295 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAPYLENE GF30HKB | Sahel Chimie Co. | PP, Unspecified | SAPYLENE |
| Ecotan B F30 FL CB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Hyundai EP PA6 LS140 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| SQUARE® LIM3600-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| REV Materials 8006 | REV Materials | Polyolefin, Unspecified | REV Materials |