WELLAMID Nylon 6000/50 HWUVCP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XXkG2X_WELLAMID-Nylon-6000-50-HWUVCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6000/50 HWUVCP is a Polyamide 6 (Nylon 6) material. It is available in Europe. Important attributes of WELLAMID Nylon 6000/50 HWUVCP are:
Typical application of WELLAMID Nylon 6000/50 HWUVCP: Automotive |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 4.00 mm | 0.80 to 1.2 | -- | % | |
| Flow : 4.00 mm | 0.80 to 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 to 3.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.5 | 25 | % | |
| Break | > 50 | > 50 | % | |
| Flexural Modulus | 1900 | -- | MPa | DIN 52457 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | 30 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 130 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 170 | -- | °C | ISO 306/B50 |
| Melting Temperature | 215 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 9.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 6.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.024 | 0.25 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 70815 | RTP Company | PP, Unspecified | RTP |
| Bergamid™ BG6000-8037 RS HS BK001 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| CALP MRP312 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Ferro PP NPP00RS02WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Geon™ Vinyl Rigid Extrusion L7005 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |