Geon™ Vinyl Flexible A5DU0
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Flexible |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XXWlyo_Geon-Vinyl-Flexible-A5DU0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Interior applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 15 sec | 90 | ||
| Shore D | 50 | ||
| Shore D, 15 sec | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Break | 20.7 | MPa | |
| 100% Strain | 15.2 | MPa | |
| Tensile Elongation 2(Break) | 340 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 118 | kN/m | ASTM D624 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -- | 800 | MPa | |
| -11°C | 310 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -21.1 | °C | ASTM D746 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 179 to 191 | °C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mold Star® 16 FAST | Smooth-On, Inc | Silicone | Mold Star® |
| Celanex® 2008 | Celanese Corporation | PBT | Celanex® |
| DENKA Transparent Polymer TE-20S | Denka Company Limited | ABS | DENKA Transparent Polymer |
| INTOL® 1509 | Versalis S.p.A. | SBR, Emulsion | INTOL® |
| INSPIRE™ 137 (Film Extrusion) | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |