LNP™ STAT-LOY™ NX13401 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XWWGvC_LNP-STAT-LOY-NX13401-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release. Also known as: LNP* STAT-LOY* Compound NX13401 Product reorder name: NX13401 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.60 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 1840 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 45.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/5 |
| Break 3 | 38.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.2 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5 |
| Break 5 | 56 | % | ASTM D638 |
| Break | 23 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1880 | MPa | ASTM D790 |
| -- 7 | 1760 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 63.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 67.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 820 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength 9(23°C) | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 38.5 | J | ASTM D3763 |
| -- | 36.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 75.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 199 to 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5940 B131 C | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Desmovit® DP R9930 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Fainplast PVC RST 0447/1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Luxus PP 16194 | Luxus Limited | PP, Unspecified | Luxus PP |
| Sylvin 8203-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |