TRIBOCOMP® PA66 CF10 TS2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XUXDI8_TRIBOCOMP-PA66-CF10-TS2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA66 CF10 TS2 is a Polyamide 66 (Nylon 66) product filled with 10% carbon fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 8800 | MPa | |
| 90°C | 3700 | MPa | |
| 120°C | 3100 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Yield, 23°C | 135 | MPa | |
| Yield, 90°C | 80.0 | MPa | |
| Yield, 120°C | 70.0 | MPa | |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | MPa | ISO 178 |
| Coefficient of Friction 1 | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.10 | ||
| vs. Itself - Static | 0.090 | ||
| Wear Factor (23°C) | 7.00 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 3.2E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.43 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 280 to 295 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 4105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Fainplast PVC RE 337 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Geon™ Vinyl Flexible D7000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 5132-86 Clear Red 6245 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® LIM8626-60A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |