Latilon 28D-V0
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTTIwv_Latilon-28D-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polycarbonate (PC). UL94 V-0 classified, with halogens, PBB/PBDE and antimonium trioxide free. Product UL certified. Low smoke toxicity index and optical density. Very high dimensional stability. Very good surface appearance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.60 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2400 | MPa | |
| 60°C | 2100 | MPa | |
| 90°C | 1800 | MPa | |
| 120°C | 1600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 65.0 | MPa | |
| Yield, 60°C | 60.0 | MPa | |
| Yield, 90°C | 50.0 | MPa | |
| Yield, 120°C | 35.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Break, 60°C | 30.0 | MPa | |
| Break, 90°C | 25.0 | MPa | |
| Break, 120°C | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 5.0 | % | |
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 3.0 | % | |
| Yield, 120°C | 2.5 | % | |
| Break, 23°C | 80 | % | |
| Break, 60°C | 70 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 37 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIZ5908A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Solprene® 4302 | Dynasol Elastomers | SBS | Solprene® |
| TOTAL Polypropylene PPC 4824WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Tufpet PBT N1000 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| INDURE™ X220-UV NAT | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |