Sinpolene CPP1030
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark: | Sinpolene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XTBbPl_Sinpolene-CPP1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sinpolene CPP1030 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% calcium carbonate. It is available in Asia Pacific for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 116 | °C | ASTM D648 |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN3611SN | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| Sindustris ABS LTR663 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| UBE Nylon 5034 MTAX1 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| DENKA POVAL B-24 | Denka Company Limited | PVOH | DENKA POVAL |
| Formolene® 6507N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |