Hanwha Total PP BI51W
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XSIRhl_Hanwha-Total-PP-BI51W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BI51W is a polypropylene compound with super weatherability and is ideal for use in outdoor products such as the exteriors of air-conditioning systems. This grade uses a base PP, such as HIPP (High Isotactic Polypropylene), and is manufactured with special processing technology to provide customers with a product of the best quality. This grade possess heightened rigidity, impact-resistance, long-term heat-resistance, as well as protection against thermal discoloration and anti-static property. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.4 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 30.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Apparent Bending Modulus | 40.2 | MPa | ASTM D747 |
| Flexural Modulus 3 | 1420 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 122 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 58.8 to 98.1 | MPa | |
| Holding Pressure | 39.2 to 88.3 | MPa | |
| Screw Speed | 30 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 121-79W233 | ExxonMobil Chemical | TPV | Santoprene™ |
| Tuftec™ H1051 | AKelastomers | SEBS | Tuftec™ |
| Fainplast PVC RK 742 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| HAIPLEN EP50 C8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Hanwha Total PP CH53W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |