Duratron® T4501

Category:	PAI , Polyamide-imide
Manufacturer:	Quadrant Engineering Plastic Products
Trademark:	Duratron®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XRyiNd_Duratron-T4501.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Duratron® T4501 compression molded PAI is well suited for general purpose wear and friction parts. It has a higher compressive strength and can therefore carry more load than Duratron® T4540. It is similar in composition to Torlon 4301 PAI, and selected when larger shapes are required.

Duratron® PAI is the highest performing melt processable plastic. It has superior resistance to elevated temperatures. It is capable of performing under severe stress conditions at continuous temperatures to 500°F (260°C). Parts machined from Duratron® stock shapes provide greater compressive strength and higher impact resistance than most advanced engineering plastics. Its extremely low coefficient of linear thermal expansion and high creep resistance deliver excellent dimensional stability over its entire use range. Duratron® PAI is an amorphous material with a Tg (glass transition temperature) of 537°F (280°C).

Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.

General Information
Features	Acid Resistant Alcohol Resistant Amorphous Good Chemical Resistance Good Compressive Strength Good Creep Resistance Good Dimensional Stability Good Stiffness Good Thermal Stability Good Wear Resistance High Impact Resistance High Strength Hydrocarbon Resistant Solvent Resistant
Uses	Bearings Bushings Seals
Forms	Customizable Forms Disc Preformed Parts Rod Tubing
Processing Method	Compression Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.45	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.30	%
Saturation	1.5	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
E-Scale	70
M-Scale	106
Durometer Hardness (Shore D)	90		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3030	MPa	ASTM D638
Tensile Strength (Ultimate)	68.9	MPa	ASTM D638
Tensile Elongation (Break)	3.0	%	ASTM D638
Flexural Modulus	4480	MPa	ASTM D790
Flexural Strength (Yield)	138	MPa	ASTM D790
Compressive Modulus	2480	MPa	ASTM D695
Compressive Strength (10% Strain)	110	MPa	ASTM D695
Coefficient of Friction (vs. Steel - Static)	0.20		Internal Method
Wear Factor	9.1	10^-8 mm³/N·m	ASTM D3702

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	27	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	279	°C	ASTM D648
Maximum Use Temperature - Long Term, Air	260	°C

Additional Information	Nominal Value	Unit	Test Method
Limiting Pressure Velocity ¹	0.788	MPa·m/s	Internal Method

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	275	°C	ASTM D3418
CLTE - Flow ²(-40 to 149°C)	3.6E-5	cm/cm/°C	ASTM E831
Thermal Conductivity	0.53	W/m/K	ASTM F433

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity ³	> 1.0E+13	ohms	Internal Method
Dielectric Constant (1 MHz)	6.00		ASTM D150
Dissipation Factor (1 MHz)	0.042		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.18 mm, Estimated Rating)	V-0		UL 94

Note Message
1 .	4:1 safety factor
2 .	68°F
3 .	EOS/ESD S11.11

Resin Grade	Manufacturer	Category	Trademark
SURPASS® IGs153-A	NOVA Chemicals	HDPE Copolymer	SURPASS®
HONES® PPS HS-G40	Guangdong Shunde Hones Polymer Material Co., Ltd.	PPS	HONES®
KumhoSunny ASA 200FR	Shanghai KumhoSunny Plastics Co., Ltd.	ASA	KumhoSunny ASA
LNP™ LUBRILOY™ D20001 compound	SABIC Innovative Plastics	PC	LNP™ LUBRILOY™
Sylvin 9648-70 Clear Black 286	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin