Celstran® PA6-GF50-01
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XRygGg_Celstran-PA6-GF50-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% long strand fiber glass reinforced nylon 6 Natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 - 0.10 | % | ASTM D955 |
| Transverse flow | 0.20 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 16000 | MPa | ASTM D638 |
| 23°C | 17600 | MPa | ASTM D638 |
| 121°C | 9030 | MPa | ASTM D638 |
| -- | 16000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 322 | MPa | ASTM D638 |
| Fracture, 23°C | 272 | MPa | ASTM D638 |
| Fracture, 121°C | 123 | MPa | ASTM D638 |
| Fracture | 245 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.6 | % | ASTM D638 |
| Fracture, 23°C | 2.2 | % | ASTM D638 |
| Fracture, 121°C | 2.3 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 390 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 39 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 270 - 275 | °C | |
| Front Temperature | 275 - 280 | °C | |
| Nozzle Temperature | 275 - 280 | °C | |
| Processing (Melt) Temp | 270 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 275 to 280°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HDPE 20 | ResMart | HDPE | ResMart Ultra |
| Selar® PA 3426R | DuPont Packaging & Industrial Polymers | Nylon 6I/6T | Selar® PA |
| Sylvin 8299-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® PA6 A 3030/109 GB30 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Durethan® BKV 50 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |