ReinForce™ 5935LE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | ReinForce™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XRup98_ReinForce-5935LE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer glass fiber and mica reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (3.00 mm) | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 40.0 | °C |
| Injection instructions |
|---|
| Hold Pressure: 400-600 barScrew Speed: 15 mm/secBack Pressure: 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50B07/P50B07-S (Single Strand) | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| StarTwist™ 315XT (transparent) | Innovia Films Ltd. | CA | StarTwist™ |
| SuperLite® SL550700-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| EPO-TEK® H35-175MPT | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| MACOMASS PP MM-PP BI 22 | MACOMASS Verkaufs AG | PP Copolymer | MACOMASS PP |