Latiblend 5262
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XR9s83_Latiblend-5262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer (PPh)/Polyamide 6 (PA 6). Very high impact resistance. Very high toughness properties. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.4 to 1.8 | % | |
| Flow : 2.00 mm | 1.3 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 750 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 22.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Break, 23°C | 150 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 350 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 70.0 | °C | |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ 1018G | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| BJB Epoxy TC-4207 A/B | BJB Enterprises, Inc. | Epoxy | BJB Epoxy |
| Jampilen EP440N | Jam Polypropylene Company | PP Copolymer | Jampilen |
| LNP™ THERMOCOMP™ MFB22EXJ compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Sylvin 913-80FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |