AvaSpire® AV-848 GF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XQfvIn_AvaSpire-AV-848-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 GF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire® PAEK can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18mm | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 10600 | MPa | ASTM D638 |
| Tensile Strength 3 | 168 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 9900 | MPa | ASTM D790 |
| Flexural Strength | 239 | MPa | ASTM D790 |
| Compressive Strength | 139 | MPa | ASTM D695 |
| Shear Strength | 84.8 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.20 mm) | 257 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | DSC |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| Specific Heat | DSC | ||
| 50°C | 1300 | J/kg/°C | DSC |
| 200°C | 1700 | J/kg/°C | DSC |
| Thermal Conductivity | 0.29 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.8E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.74 | ASTM D150 | |
| 1 MHz | 3.69 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 6.0E-3 | ASTM D150 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 60.0 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 382 - 404 | °C | |
| Mold Temperature | 166 - 193 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Back Pressure: Minimum |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 200°C,2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE HP4023W | SABIC Americas, Inc. | LDPE | SABIC® LDPE |
| Sanren F500EP (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Rotec® ABS 5001/05 | ROMIRA GmbH | ABS | Rotec® ABS |
| EcoBlend® HCL7120 | Shanghai KumhoSunny Plastics Co., Ltd. | PLA+PMMA | EcoBlend® |
| Huafon JF-P-5175 / JF-I-5118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |