INEOS HDPE K54-05
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XQDkH4_INEOS-HDPE-K54-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| K54-05 is a high molecular weight, high density polyethylene copolymer intended for blow molding large parts such as drums. It combines excellent processability and a good balance of stiffness, environmental stress crack resistance (ESCR) and impact properties. This resin meets the Food and Drug Administration requirements of 21CFR 177.1520 for contact with food. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| 10% Igepal, F50 | 140 | hr | ASTM D1693B |
| 100% Igepal, F50 | 1800 | hr | ASTM D1693A |
| 100% Igepal, F50 | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.6 | MPa | |
| Break | 41.4 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.0 | % | |
| Break | 900 | % | |
| Flexural Modulus | ASTM D790A | ||
| 2% Secant | 1050 | MPa | |
| Tangent | 1410 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 700 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 69.3 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 47.2 | °C | |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A400MX01 | Toray Resin Company | PPS | Torelina® |
| 4PROP® 9D02430 UV | 4Plas | PP Homopolymer | 4PROP® |
| LG PMMA EG920B | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Hifax TRC 277P S71487 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 5145-75 Clear Red 6192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |