Polyamide 66, Un-Filled material, red pigmented for injection molding |
General Information | |
---|---|
Appearance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow | 1.5 to 1.8 | % | Internal Method |
Water Absorption (Equilibrium) | 1.3 | % | ASTM D570 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness | ASTM D785 | ||
M-Scale | 80 | ||
R-Scale | 115 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 10 | % | ISO 527-2 |
Flexural Modulus | 2500 | MPa | ISO 178 |
Flexural Stress | 120 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | 49.0 | J/m | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
Melting Temperature | 260 | °C | DSC |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
Dielectric Strength | 21 | kV/mm | ASTM D149 |
Comparative Tracking Index | > 600 | V | IEC 60112 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 80.0 | °C | |
Drying Time | 2.0 to 4.0 | hr | |
Suggested Max Moisture | 0.20 | % | |
Processing (Melt) Temp | 280 to 300 | °C | |
Mold Temperature | 40.0 to 80.0 | °C | |
Injection Pressure | 3.50 to 12.5 | MPa | |
Injection Rate | Fast |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Manner Flexible PVC X4077 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
ALCUDIA® LDPE PE-071 | REPSOL | LDPE | ALCUDIA® LDPE |
API PS 392 | American Polymers, Inc. | PS (GPPS) | API PS |
Sylvin 9266-70 Grey 9513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
Rotec® ABS 1200 TR-AC | ROMIRA GmbH | ABS | Rotec® ABS |