PEARLCOAT® 125K

Category:	TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester)
Manufacturer:	Lubrizol Advanced Materials, Inc.
Trademark:	PEARLCOAT®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XNwkCl_PEARLCOAT-125K.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PEARLCOAT® 125 K is a polyester-based TPU, supplied in form of translucent, colourless pellets, featuring medium softening point, and consistent quality pellets, low gel content as well low-temperature flexibility.

PEARLCOAT® 125K is used in a wide range of applications:

Melt coatings on textile substrates, for conveyor belts, belting, etc, end uses, obtained by extrusion, calendering or sintering (in this last case the product is previously ground, so as to be in powder form).

Extruded films and fabric coatings.

Low melting point carrier for TPU colour and additives masterbatches

General Information
Features	Low speed solidification crystal point Flexibility at low temperatures
Uses	Films Conveyor belt repair Conveyor accessories Textile applications Masterbatch Coating application Fabric
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 177.2600
Appearance	Translucent Colorless
Forms	Particle
Processing Method	Film extrusion Extrusion Sintering Calendering

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--	1.20	g/cm³	ASTM D792
20°C	1.20	g/cm³	ISO 2781
Moisture Content	< 1000	ppm	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	85		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Abrasion Loss	25.0	mm³	ISO 4649

Extrusion	Nominal Value	Unit
Extruder Screw L/D Ratio	25:1
Extruder Screw Compression Ratio	3:1

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412, ISO 527
100% strain	6.00	MPa	ASTM D412, ISO 527
300% strain	9.00	MPa	ASTM D412, ISO 527
Tensile Strength (Yield)	30.0	MPa	ASTM D412, ISO 527
Tensile Elongation (Break)	5500	%	ASTM D412, ISO 527

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-27.0	°C	ISO 11357-2
Melting Temperature ¹	135 - 145	°C	Internal method

Extrusion	Nominal Value	Unit
Drying Temperature	90.0 - 100	°C
Drying Time	1.0 - 2.0	hr
Cylinder Zone 1 Temp.	150 - 160	°C
Cylinder Zone 2 Temp.	160 - 170	°C
Cylinder Zone 3 Temp.	170 - 180	°C
Cylinder Zone 4 Temp.	175 - 185	°C
Die Temperature	175 - 185	°C

Extrusion instructions
Cooling: AirSpeed: 50 rpmThickness Die: 0.2 mm

Note Message
1 .	Temperature at which MFI = 10 g/10 min @ 21.6 kg

Resin Grade	Manufacturer	Category	Trademark
Shandong PP PG8301	Shandong Dongchen Engineering Plastics Co., Ltd.	PP, Unspecified	Shandong PP
Bayblend® FR630 GR	Covestro - Polycarbonates	PC+ABS	Bayblend®
ALTECH® ABS A 1000/100	ALBIS PLASTIC GmbH	ABS	ALTECH® ABS
Sylvin 9915-87 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Sylvin 9710-80FUV Grey 9497	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin