TOTAL Polyethylene Lumicene® M 2710 EP (US)
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XNEalD_TOTAL-Polyethylene-Lumicene-M-2710-EP-US-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene mPE M 2710 EP (US) is a Polyethylene material. It is available in Asia Pacific or North America for film extrusion. Important attributes of TOTAL Polyethylene mPE M 2710 EP (US) are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.927 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.90 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Static) | 0.50 | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882A | ||
| 1% Secant, MD : 25 µm, Blown Film | 214 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 172 | MPa | |
| Tensile Strength | ASTM D882A | ||
| MD : Break, 25 µm, Blown Film | 33.8 | MPa | |
| TD : Break, 25 µm, Blown Film | 33.1 | MPa | |
| Tensile Elongation | ASTM D882A | ||
| MD : Break, 25 µm, Blown Film | 580 | % | |
| TD : Break, 25 µm, Blown Film | 720 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 170 | g | |
| TD : 25 µm, Blown Film | 500 | g | |
| Seal Initiation Temperature (25 µm, Blown Film) | 112 | °C | |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 14 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 121 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (45°, 25.4 µm, Blown Film) | 65 | ASTM D523 | |
| Haze (25.4 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer T-500 | Shanghai Potomer International Trade Co., Ltd. | CPVC | Shanghai Potomer |
| ASTALON™ H3000UR | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Fainplast PVC GS 01141 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DuraFlex 403-2 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Karina BLACK PVC COMPOUND 807D48/ 1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |