Clearflex® H&T CL 506
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XMMySX_ClearflexHampTCL506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex CL 506 is an hexene copolymer linear medium density polyethylene (C6-LMDPE), with antioxidants, suitable for cast film extrusion. Films manufactured with Clearflex CL 506 exhibit a good balance between rigidity and stretchability. Main Applications Clearflex CL 506 is recommended for the production of film characterized by good mechanical resistance and high rigidity (hygienic film). Its high Vicat softening point makes Clearflex CL 506 the ideal choice for the production of films for food which are submitted to pasteurisation or sterilisation process. Clearflex XL 506 is ideal choice for the production of artificial grass. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : 23 µm, cast film | 300 | MPa | ISO 527-3 |
| 1% sectioning, TD : 23 µm, cast film | 350 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 23 µm, cast film | 16.0 | MPa | ISO 527-3 |
| TD : yield, 23 µm, cast film | 17.0 | MPa | ISO 527-3 |
| MD : fracture, 23 µm, casting film | 35.0 | MPa | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : fracture, 23 µm, casting film | 650 | % | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 800 | % | ISO 527-3 |
| Dart Drop Impact (23 µm, Cast Film) | 40 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 23.0 µm | 20.0 | kN/m | ISO 6383-2 |
| TD : 23.0 µm | 80.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 | °C | ISO 306/A |
| Melting Temperature | 129 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 80 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 4.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 270 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megalon® 143GL | Mega Polymers | Nylon 66 | Megalon® |
| Wah Hong UP WH-8100-BLK F | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| Aplax P2515GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| FRIANYL® C3 GF10 TF20 V2XI | Nilit Plastics | Nylon 66/6 | FRIANYL® |
| Hostacom PPR 1042 HL21S | LyondellBasell Industries | PP Copolymer | Hostacom |