MarFlex® 7105D
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XLEgSZ_MarFlex-7105D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex®7105D is a linear low density polyethylene material,. This product is available in North America or Latin America. The processing method is blow molded film. MarFlex®The main features of 7105D are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.5 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 200 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 59.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 43.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 550 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 710 | % | ASTM D882 |
| Dart Drop Test - Blown Film (25.4 µm) | 193.0 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.4 µm | 162.2 | kN/m | ASTM D1922 |
| TD : 25.4 µm | 231.7 | kN/m | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 90 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Blown Film produced on 3.5 in extruder, 30:1 L/D, 8 in Die, 80 mil Die Gap, 2.5:1 BUR, 440°F Melt Temperature. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200H AR 15 | RTP Company | Nylon 66 | RTP |
| RxLOY™ NPP00NP03NA | Ferro Corporation | PP Copolymer | RxLOY™ |
| SABIC® HDPE F0863 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| UBE Polyethylene F019 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Unichem 84-421D | Colorite Polymers | PVC, Unspecified | Unichem |