RTP VLF 80211 EM HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XLELnB_RTP-VLF-80211-EM-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long Glass Fiber - Easy Molding - Heat Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22400 | MPa | ASTM D638 |
| Tensile Strength | 276 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.5 - 2.5 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength | 414 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 530 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 243 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 271 - 299 | °C | |
| Mold Temperature | 65.6 - 124 | °C | |
| Injection Pressure | 34.5 - 124 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 0.5.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| RTP 1300 AR 15 TFE 15 | RTP Company | PPS | RTP |
| AEROPASTE® 1006 | Cytec Industries Inc. | Adhesive | AEROPASTE® |
| Geon™ Vinyl Wire & Cable WR3792CL | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Innothane® FM-109 | Innovative Polymers, Inc. | TSU | Innothane® |