TOTAL Polypropylene PPH 10042
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XIfVxt_TOTAL-Polypropylene-PPH-10042.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 10042 is a nucleated antistatic homopolymer with a high Melt Flow Index of 35 g/10 min. Polypropylene PPH 10042 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots & tubs, salad trays and caps & closures. Polypropylene PPH 10042 is nucleated and thus has improved rigidity. This coupled with a highly antistatic nature allows for shorter cycle times and easy demoulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.5 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 A TFE 10 | RTP Company | PC+Acrylic | RTP |
| RheTech Thermoplastic Polyolefin FT4900-74UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Shuang-Bang WM-8157N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| STERLENE™ CMV207 | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Axiall PVC 1854 Blue 107 | Axiall Corporation | PVC, Flexible | Axiall PVC |