ESTOPLAST XU 5230BB11
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | ESTOPLAST XU |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XIIp1D_ESTOPLASTXU5230BB11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 - Toughened, Glass Fiber Reinforced, 30% Automotive: Wheel Assembly, Exterior trim, Interior trim, Electrical components and connectors Electrical & Electronic: Low voltage switch gear/power distribution, Lighting, Power connectors , MCCB, |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.95 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 131 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 200 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 27 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 235 - 245 | °C | |
| Middle Temperature | 245 - 255 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 240 - 250 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP151T | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| Clyrell RC1908 | LyondellBasell Industries | PP Copolymer | Clyrell |
| Karina WHITE COLOR CONCENTRATE -E 10/ 85-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ XM-7070S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |
| Evoprene™ G 618 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ G |