LOFEX® A31AA
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XHTUQL_LOFEX-A31AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A31AA is Polyester film is optically clear and both sides acryl treated with enhanced adhesion to inks and coatings. So, it can use by graphic, membrane switch, label, circuit board. It has excellent properties by tensile strength, proper elongation and the thermal contraction rate. Also, it is a product that thickness control is possible according to customer needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.30 | ||
| vs. Itself - Static | 0.35 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| MD : Yield, 130 µm | 186 | MPa | |
| MD : Yield, 190 µm | 177 | MPa | |
| TD : Yield, 50 µm | 216 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| TD : Yield, 130 µm | 216 | MPa | |
| TD : Yield, 190 µm | 216 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 160 | % | |
| MD : Break, 100 µm | 170 | % | |
| MD : Break, 130 µm | 170 | % | |
| MD : Break, 190 µm | 170 | % | |
| TD : Break, 50 µm | 110 | % | |
| TD : Break, 100 µm | 120 | % | |
| TD : Break, 130 µm | 120 | % | |
| TD : Break, 190 µm | 120 | % | |
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| MD : 125.0 µm | 113 | MPa | |
| MD : 188.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa | |
| TD : 125.0 µm | 113 | MPa | |
| TD : 188.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 125.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 188.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 125.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 188.0 µm | 0.50 | % | |
| Surface Treatment | Both sides (Acryl) |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 170 | ||
| 60°, 100 µm | 170 | ||
| 60°, 125 µm | 170 | ||
| 60°, 188 µm | 170 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 89.0 | % | |
| 100 µm | 89.0 | % | |
| 125 µm | 89.0 | % | |
| 188 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 1.3 | % | |
| 100 µm | 2.1 | % | |
| 125 µm | 2.4 | % | |
| 188 µm | 2.7 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XWB-3330 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Zhongfa PP pp2 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Dynaprene® VE0080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| OmniLon™ PA6/6 MS2 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| LNP™ LUBRICOMP™ LL004C compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |