RIGITRON 30545 GF
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | RIGITRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XGoKl8_RIGITRON-30545-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyester - 45% Glass Fiber Reinforced PET. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 0.0 to 0.20 | % | |
| Across Flow : 3.17 mm | 0.0 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10800 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 168 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 4 | 13500 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 220 | °C | ASTM D648 |
| Peak Melting Temperature 6 | 250 to 258 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 15°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP514-447UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| AMTOPP CM15 | Inteplast Group | PP, Unspecified | AMTOPP |
| Desmopan® DP 2786A | Covestro - PUR | TPU-Polyester | Desmopan® |
| Eltex® P KS351 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Karina BLACK PVC COMPOUND E-CAK 60-48/1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |