KOPLA PA6 KNT1020
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XGEzAs_KOPLA-PA6-KNT1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KNT1020 is a Polyamide 6 (Nylon 6) material filled with mineral. It is available in Asia Pacific. Important attributes of KOPLA PA6 KNT1020 are:
Typical application of KOPLA PA6 KNT1020: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3920 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 185 | °C | |
| 1.8 MPa, Unannealed | 140 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXATEC™ 4115 | SAX Polymers | ASA | SAXATEC™ |
| TAIRIREX GP525N | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| XANTAR® 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Estane® R195A-9 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Huafon JF-W-DP4050 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |