Niblan V100 AE V0/M
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niblan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XFyRBe_Niblan-V100-AE-V0-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced PBT, impact modified and flame retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 - 2.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 2500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -22°C, 3.20 mm | 35 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | °C | ASTM D3418 |
| CLTE - Flow (23 to 55°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Volume Resistivity, IEC 60093: >1E15 ohm-cmSurface Resistivity, IEC 60093: >1E15 ohms |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EPH30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| Daelim Po1y® PP-137 | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Geon™ Vinyl Rigid Extrusion 87775 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| HOPELEX PCH-2006 | Lotte Chemical Corporation | PC | HOPELEX |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |