Solef® 6008
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XEx62u_Solef-6008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 6008 PVDF homopolymer is a low-viscosity PVDF resin and is typically processed by injection molding. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/2.16 kg | 5.5 to 11 | g/10 min | |
| 230°C/5.0 kg | 16 to 30 | g/10 min | |
| Molding Shrinkage - Flow | 2.0 to 3.0 | % | |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 2.00 mm) | 73 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 1800 to 2500 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 50.0 to 60.0 | MPa | |
| Break, 23°C, 2.00 mm | 30.0 to 50.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 5.0 to 10 | % | |
| Break, 23°C, 2.00 mm | 20 to 300 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.15 to 0.35 | ||
| vs. Itself - Static | 0.20 to 0.40 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 10.0 | mg | ASTM D4060 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C, 4.00 mm) | 40.0 to 120 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
| Vicat Softening Temperature | 135 to 145 | °C | ASTM D1525 5 |
| Melting Temperature | 170 to 175 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 134 to 144 | °C | ASTM D3418 |
| CLTE - Flow (0 to 40°C) | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | ASTM E968 | ||
| 23°C | 1200 | J/kg/°C | |
| 100°C | 1600 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ASTM C177 |
| Crystallization Heat | 54.0 to 60.0 | J/g | ASTM D3417 |
| Heat of Fusion | 58.0 to 67.0 | J/g | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 kHz) | 7.00 to 10.0 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.200 mm) | V-0 | UL 94 | |
| Oxygen Index (3.00 mm) | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Type IV, 1.0 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 2 m/s |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 680 | RTP Company | ABS | RTP |
| Sylvin 8210-85C White 1487 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRIBIT® 1500A15 | Samyang Corporation | PBT | TRIBIT® |
| Karina CLEAR PVC COMPOUND 65/205-DA-IS-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| WELLAMID Nylon 6600 GS 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |