Ultrason® E 2010 G4 MR SW 15102
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XEYPMx_Ultrason-E-2010-G4-MR-SW-15102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultrason® pellets are supplied in bags and/or octabins. The bulk density ranges between 700 and 800 g/l. Provided the packaging remains undamaged, Ultrason® can be stored indefinitely. Ultrason® pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 4h at 130°C to 150°C in a vacuum or dry air drier prior to processing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 29.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.61 | % | |
| Flow | 0.36 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.6 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % | |
| Viscosity Number 1 | 56.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 205 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 47 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 6.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 225 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| 180°C | 2.3E-5 | cm/cm/°C | DIN 53752 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Polymer Abbreviation | PESU-GF20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 300 | mm/sec | |
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 350 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 370 | °C | |
| Nozzle Temperature | 370 | °C | |
| Processing (Melt) Temp | 350 to 390 | °C | |
| Mold Temperature | 150 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X689 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Zhongfa PET G30FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| EPO-TEK® OG603 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hyundai EP XLPE XP670/Natural | HYUNDAI EP Co., Ltd. | XLPE | Hyundai EP XLPE |
| LGSTRENE LGH 308 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGSTRENE |