Capilene® G 86 E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XE5gmZ_Capilene-G-86-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® G 86 E is a polypropylene homopolymer intended for extrusion and thermoforming applications. CAPILENE ® G 86 E features: low water carry-over, good processability. CAPILENE ® G 86 E is suitable for: raffia, tapes, strapping, carpet backing, thermoforming; injection molding of technical items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 36.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 11 | % | ASTM D638 |
| Yield | 11 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1550 | MPa | ASTM D790 |
| -- 3 | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 132G | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Novamid® 2430AH2 | DSM Engineering Plastics | Nylon 66/6 | Novamid® |
| BONDINE® HX8210 | Arkema | EAA | BONDINE® |
| Generic PP Homopolymer - Glass Fiber | Generic | PP Homopolymer | Generic |
| Latimass 52/11-01 D020 | LATI S.p.A. | PP Homopolymer | Latimass |