INNOPOL® PP CS 1-7120
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XDCovk_INNOPOL-PP-CS-1-7120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL ® CS 1-7120 is a 20 % talc-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-7120 is recommended for extrusion of sheets and profiles, where one of the required properties is good stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 18 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 115 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 260 | °C | |
| Middle Temperature | 190 - 260 | °C | |
| Front Temperature | 190 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 15.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold Pressure: 50 to 100% of injection pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Cylinder Zone 5 Temp. | 180 - 220 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 190 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoFin TV 30 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| NORYL™ PVX0901 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Novalloy-B B2404 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Elastron® G G100.D35.B | Elastron USA, Inc. | SEBS | Elastron® G |
| LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |