ENGAGE™ 8137
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XCwwQg_ENGAGE-8137.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™8137 polyolefin elastomer is an ethylene-octene copolymer with low density and high melt index. This combination of properties enables ENGAGE 8137 to have excellent toughness, flexibility and simple processing, and can be used as an efficient impact modifier in polyolefins or as a component in injection molding processing. Main features:
Application field:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.864 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 4 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 63 | ASTM D2240 | |
| Shore D, 1 second, molded | 13 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.80 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 2.40 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 7.80 | MPa | ASTM D790 |
| 2% secant : Molding | 7.30 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 26.4 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -55.0 | °C | Internal method |
| Melting Temperature (DSC) 5 | 56.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 38.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Relpet® QH5821 | Reliance Industries Limited | PET | Relpet® |
| SIVIC® 2710 | SIDIAC | PVC+NBR | SIVIC® |
| WELLAMID Nylon 6000 GS 30 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| EPIMIX POM PTFE 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| Sylvin 8310-75C UV White 1507 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |