Arylmax® P7000
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Arylmax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XCvIrq_Arylmax-P7000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketone with Tg of 446°F (230°C) |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 98.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 230 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 380 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 200 to 210 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-124-28 | Quantum Composites Inc. | TS, Unspecified | Quantum Composites |
| Unipren® Elastomers B3 NTLA010 55A UP310 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Chemraz 505 | Greene, Tweed & Co. | PTFE | Chemraz |
| Laticonther 62 CEG/500-V0HF1 | LATI S.p.A. | Nylon 6 | Laticonther |
| Hostacom CR 1171 G1 G74010 | LyondellBasell Industries | PP Copolymer | Hostacom |