SABIC® PP FPC55
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XCtfxQ_SABIC-PP-FPC55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP FPC55 is a grade developed for the thin wall packaging market. The grade is nucleated and is characterised by excellent flow behaviour in combination with an improved stiffness to impact balance. SABIC® PP FPC55 allows for very cost efficient processing on the basis of easy mould filling, short cycle times and improved part consistency in combination with pigments. It contains an antistatic package. SABIC® PP FPC55 is typically used in thin wall packing applications both for food and non-food segments. This includes pails & containers, yellow fats/margarine tubs and dairy cups. In de caps and closure segment, the grade could be used for thin walled spray through caps, amongst other. The grade has excellent heat deflection temperature making it particularly suitable for hot fill applications. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 | |
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1550 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 24.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | |
| 0°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C | 45 | J/m | ASTM D256A |
| 0°C | 60 | J/m | ASTM D256A |
| 23°C | 70 | J/m | ASTM D256A |
| -20°C | 5.0 | kJ/m² | ISO 180/1A |
| 0°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 76.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® G11 | ITEN INDUSTRIES | Phenolic | Resiten® |
| Thermoset Plastics 125 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| LubriOne™ ATC-000/20T BLACK UV | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| Moplen HP504N | LyondellBasell Industries | PP Homopolymer | Moplen |
| Delene 3580 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |