LNP™ STAT-KON™ CD000 compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XBHDgR_LNP-STAT-KON-CD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON CD000 is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound CE Product reorder name: CD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.70 to 1.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 26.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 11 | kJ/m² | ISO 180/1A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT SIGNATURE PA6 G33-100 | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT SIGNATURE |
| Cheng Yu A706G15 | Cheng Yu Plastic Company Limited | SAN | Cheng Yu |
| CP PRYME® Nylon 66 NN233HL-ES BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Dyna-Purge® SF | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
| Sylvin 8200-70 Grey 9539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |