POLYfill PPH GF5030 PD2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X9n9TE_POLYfill-PPH-GF5030-PD2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glassfibre-reinforced Chemically coupled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.25 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5600 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 127 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 M30 | NUREL, S.A. | Nylon 6 | Promyde® |
| WELLAMID Nylon 6600 GS 20 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| TULAMID® PA-SV30-L1 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| NuSil MED-4850 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| POLYCASA® ACRYL KR 2007/1 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |