NYCOA Polyamide 1485 HS
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X9EXzz_NYCOA-Polyamide-1485-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 1485 HS is a heat stabilized Nylon copolymer TPE which offers outstanding toughness, flexibility, and strength. It is particularly suitable for extrusion processing. The chemical composition of NYCOA 1485 HS delivers improved impact performance at ambient or low temperatures, and increased flexibility to meet higher impact performance. The high thermal and chemical resistance, inherent to Nylon 6, is retained. The chemistry of the resin promotes good adhesion to olefins and other materials. This product is available with custom additive packages: UV stabilizer, flame retardant and custom colors. Typical applications include convoluted tubing, complex profiles, and pipe extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 600 | MPa | ASTM D790 |
| Flexural Strength 4 | 22.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 205 | °C |
| Additional Information |
|---|
| Water Extractable, NYCOA Method: 4 to 6 %Melt Flow Index, ASTM D1238, 235°C/1kg: 2 to 4 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 350A0096914 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Tisakril® ABS UNR | Tisan | ABS | Tisakril® |
| KOPA® KN333HI4BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina IVORY PVC COMPOUND 105800-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYCOMPO PP K7000 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |