Shinite® PBT D202G30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shinkong Synthetic Fiber Corp. |
| Trademark: | Shinite® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X8mdUk_Shinite-PBT-D202G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinite® PBT D202G30 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America. Important attributes of Shinite® PBT D202G30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 1.3 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9380 | MPa | ASTM D638 |
| Tensile Strength | 137 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength | 196 | MPa | ASTM D790 |
| Compressive Strength | 168 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 208 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | DSC |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.90 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 241 to 260 | °C | |
| Mold Temperature | 60.0 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD CR102 | Pooya Polymer Tehran | PP Homopolymer | POYAD |
| Cellidor CP 410-11 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| Gallonprene® GP410-7503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Elastollan® C 74 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Hifax CA 197 J WHITE | LyondellBasell Industries | TPO (POE) | Hifax |