SCHULAMID® 6 GF 15 HV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X8lTpC_SCHULAMID-6-GF-15-HV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fibre reinforced Polyamide 6 with high viscosity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 2.4 | -- | % | ISO 62 |
| Viscosity Number | 170 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5700 | 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | 65.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.5 | 14 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 4400 | -- | MPa | ISO 178 |
| Flexural Stress | 170 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 7.0 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 7.0 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | |
| 23°C | 62 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 AR 10 HS | RTP Company | Nylon 66 | RTP |
| Genestar™ G1350A-M42 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Karina CLEAR PVC COMPOUND -E 80/278-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PC-ABSCOM™ B200 | Polymer Compounders Limited | PC+ABS | PC-ABSCOM™ |
| OTECH ALLOY OL8540 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |