LNP™ LUBRICOMP™ RFG16 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X8g8GO_LNP-LUBRICOMP-RFG16-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP RFG16 is a compound based on PA 66 resin containing Glass Fiber, Graphite. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.24 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 156 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8700 | MPa | ISO 178 |
| Flexural Stress | 249 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 3.8 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 60 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Fainplast PVC GS 58/O | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ VERTON™ MVL36SX0 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ VERTON™ |
| Sylvin 8915-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8707-80 Blue 8467 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |